Orienteeritud kihtidega puitlaastplaadi füüsikalis mehaaniliste omaduste muutuste uurimine väikese arvu vananemise perioodide tõttu
| dc.contributor.advisor | Lille, Harri | |
| dc.contributor.advisor | Kask, Regino | |
| dc.contributor.author | Leppik, Taimo | |
| dc.date.accessioned | 2020-06-12T06:35:11Z | |
| dc.date.available | 2020-06-12T06:35:11Z | |
| dc.date.defensed | 2020-06-18 | |
| dc.date.issued | 2020 | |
| dc.description | Ehitusinseneriõppe lõputöö Maaehituse õppekaval | est |
| dc.description.abstract | Magistritöö eesmärgiks oli uurida OSB/3 plaadi füüsikalisi ja mehaanilisi karakteristikuid (paindetugevus, -elastsusmoodul, pinnakõvadus, paksusesse pundumine) korduvate, kuid siiski piiratud arvu ligunemis-, kuivamis- ja külmumisperioodide tõttu. Antud töö katsekehad lõigati piki- ja ristisuunas kolmest identsest SWISS KRONO poolt toodetud OSB/3 plaadist mõõtmetega 2500 x 1250 x 12 mm, seejärel märgistati ja mõõdeti geomeetrilised parameetrid. Järgnevalt sooritati katsekehadega kuus kiirendatud vanandamisperioodi, mis koosnesid neljast erinevast etapist (72 -tunnine vees ligunemine, 48 -tunnine kuivatamine, 24 -tunnine külmutamine, 96 -tunnine konditsioneerimine 65% õhuniiskuse juures). Pärast iga etapi läbimist eemaldati osa katsekehi (pikisuunas lõigatult 6 tk ja ristisuunas lõigatult 6 tk, kokku seerias 12 tk) ringlusest ja sooritati katsed universaalsel katsemasinal INSTRON 3369. Seda kasutati nii paindetugevuse, -elastsusmooduli kui ka pinnakõvaduse leidmiseks. Joonmöötmed pundumise määramiseks mõõdeti mikromeetriga. On esitatud katsetulemuste lähenduskõverad, mis lubavad prognoosida plaadi paindetugevuse, -elastsusmooduli ja pinnakövaduse taluvuspiirid ning pundumise lagiväärtuse. Antud magistritöö tulemuseks saadi, et peale esimest ligunemis- ja kuivamisperioodi kaotasid kõik katsekehad kõige enam oma algnäitajatest (elastsusmoodul kuni 73%, paindetugevus kuni 69%, pinnakõvadus kuni 61%, paksusesse pundumine suurenes kuni 23%). Alates teisest vanandamisperioodist vähenesid pinnakõvaduse, -elastsusmooduli ja paindetugevuse tulemused aeglasemalt. Pundumine suurenes antud katsetes kolmanda perioodini, siis stabiliseerus. Töös saadud tulemusi kõrvutati magistritöödes (vt Kallau, 2014, Telling, 2019) toodutega. | est |
| dc.description.abstract | The aim of this Master’s thesis is to study the physical and mechanical characteristics (bending, strength, elastic modulus, surface hardness, swelling) of the OSB/3 plate with repeated, but with a limited amount of periods of soaking, drying and freezing. The samples were cut longitudinally and horizontally from three identical OSB/3 plates made by SWISS KRONO, which measured 2500 x 1250 x 12 mm, after which they were labeled and their geometric parameters were measured. Then six accelerated ageing periods were conducted, which consisted of four different stages (72 hours of soaking in water, 48 hours of drying, 24 hours of freezing, 96 hours of air conditioning in 65% air humidity). After each stage some of the samples were removed (six cut longitudinally and six cut horizontally, 12 in total) from the circulation and the tests were conducted on the universal testing machine INSTRON 3369. It was used to find out the bending strength, elastic modulus, surface hardness of the samples. For the assessment of swelling the dimensions of the samples were measured with a micrometer. Convergence curves of the test results were presented, which allow to predict the tolerance limits of the plates bending strength, elastic modulus and surface hardness and the maximum of swelling. The result of this Master’s thesis was that after the first period of soaking and drying of the test samples they lost the most of their initial characteristics (elastic modulus up to 73%, bending strength up to 69%, surface hardness up to 61%, and swelling increased up to 23%). After the secondary ageing period bending strength, elastic modulus, surface hardness decreased more slowly. Swelling increased until the third ageing period and then stabilised. Results were compared with results from other Master;s theses (see Kallau, 2014, Telling, 2019). | eng |
| dc.identifier.uri | http://hdl.handle.net/10492/6047 | |
| dc.publisher | Eesti Maaülikool | |
| dc.subject | magistritööd | est |
| dc.subject | pinnakõvadus | est |
| dc.subject | paindetugevus | est |
| dc.subject | paindeelastsusmoodulid | est |
| dc.subject | pundumine | est |
| dc.subject | kiirendatud vanandamine | est |
| dc.subject | Roheline Ülikool (töö toetab EMÜ Rohelise Ülikooli põhimõtteid) | est |
| dc.subject | ehitusmaterjalid | est |
| dc.subject | looduslikud materjalid | est |
| dc.subject | ökomajad | est |
| dc.subject | säästev tehnoloogia | est |
| dc.title | Orienteeritud kihtidega puitlaastplaadi füüsikalis mehaaniliste omaduste muutuste uurimine väikese arvu vananemise perioodide tõttu | est |
| dc.title.alternative | Investigation of changes of physical-mechanical properties of oriented strand board during short ageing periods | est |
| dc.type | Master Thesis | eng |
| rioxxterms.freetoread.startdate | 18.09.2020 |